| 化學成分, % | |||||||||
|
(C) |
(Si) |
(Mn) |
(S) |
(P) |
(Cr) |
(Ni) |
(Cu) |
(Mo) |
(V) |
| ≤ | |||||||||
| ≤0.12 | 0.50-0.80 | 1.3-1.7 | 0.025 | 0.035 | 0.3 | 0.3 | 0.3 | 0.08 | 0.05 |
| 厚度mm | 機械性能 | ||||||
| 屈服強度 | 抗拉強度 | 伸長率 | 沖擊強度,KCU,J / cm2,不小于 | ||||
| , 0С | -40 | -70 | 機械老化后的溫度為 , 0С | ||||
| 從5到10 | 345Mpa | 490-640Mpa | 21 | 64 | 39 | 34 | 29 |
| 從10到20 | 325Mpa | 470-640Mpa | 21 | 59 | 34 | 29 | 29 |
| 材質 | 厚度 | 寬度 | 長度 | 塊數 | 單重 | 總重 | 備注 |
| 09G2S | 137mm | 818mm | 80376 | 10 | 1.884 | 18.84 | Te=厚*寬*長 |
| 09G2S | 10mm | 2500mm | 12000 | 5 | 2.355 | 11.775 | 舞鋼 |
| 09G2S | 12mm | 2500mm | 12000 | 5 | 2.826 | 14.13 | 舞鋼 |
| 09G2S | 16mm | 2800mm | 12000 | 10 | 4.220 | 42.2 | 河南舞鋼 |
| 09G2S | 137mm | 818mm | 80376 | 2 | 70.708 | 141.416 | Te=厚*寬*長 |
| 09G2S | 150mm | 1500mm | 11000 | 1 | 19.429 | 19.429 | 河南舞鋼 |
| 09G2S | 25mm | 2200mm | 12000 | 1 | 5.181 | 5.181 | 河南尊信 |
| 09G2S | 18mm | 2000mm | 12000 | 1 | 3.391 | 3.391 | 舞鋼 |
| 09G2S | 20mm | 1800mm | 12000 | 1 | 3.391 | 3.391 | 河南尊信 |
| 09G2S | 22mm | 1900mm | 12000 | 1 | 3.938 | 3.938 | 舞鋼 |
| 09G2S | 24mm | 2200mm | 12000 | 1 | 4.974 | 4.974 | 河南舞鋼 |
在線客服：